brazing

brazing
Process for joining two pieces of metal by applying heat and adding a filler metal.

The filler, which has a lower melting point than the metals to be joined, is either pre-placed or fed into the joint as the parts are heated. In brazing parts with small clearances, the filler is able to flow into the joint by capillarity. The temperature of the molten filler in brazing exceeds 800°F (430°C). In soldering, a related process, the filler metal remains below that temperature. Brazed joints are usually stronger than soldered joints. Most metals can be brazed, and the range of available brazing alloys has increased as new alloys and new service requirements are introduced. Brazed joints are highly reliable and are used extensively on rockets, jet engines, and aircraft parts. See also welding.

* * *

      process for joining two pieces of metal that involves the application of heat and the addition of a filler metal. This filler metal, which has a lower melting point than the metals to be joined, is either pre-placed or fed into the joint as the parts are heated. In brazing parts with small clearances, the filler is able to flow into the joint by capillary action. The temperature of the molten filler used for brazing exceeds 800° F (430° C). In a related process called soldering, the filler metal remains below that temperature. Brazed joints are usually stronger than soldered joints.

      Brazing can be carried out on most metals, and the range of available brazing alloys is increasing as new alloys and new service requirements are introduced. Heating by torch in air is satisfactory, provided the joint is adequately fluxed (flux). Other forms of heating include inductive heating, electrical resistance, molten salts, and baths of molten metal. The wide use of these processes has led to the development of special furnaces and automatic equipment, with special attention being given to accurate control of the temperature and regulation of the atmosphere. Jigs and fixtures are necessary for dip brazing. Preparation of the surfaces by mechanical or chemical cleaning is important for brazing. The extensive use of silver-based brazing alloys melting at temperatures below 1,200° F (650° C) required development of fluxes that are fluid and active at 1,100° F (593° C). Combinations of borates, fluoborates, fluorides, chlorides, borax, and boric acid are commonly used as fluxes. Brazed joints are highly reliable and are used extensively on rockets, jet engines, and aircraft parts. See also welding.

* * *


Universalium. 2010.

Игры ⚽ Нужно решить контрольную?

Look at other dictionaries:

  • Brazing — Brazing. См. Пайка твердым припоем. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • Brazing — This article is about the metal joining process. For the cooking technique, see braising. Brazing practice Brazing is a metal joining process whereby a filler metal is heated above and distributed between two or more close fitting parts by… …   Wikipedia

  • Brazing — Braze Braze, v. i. [imp. & p. p. {Brazed}; p. pr. & vb. n. {Brazing}.] [F. braser to solder, fr. Icel. brasa to harden by fire. Cf. {Brass}.] 1. To solder with hard solder, esp. with an alloy of copper and zinc; as, to braze the seams of a copper …   The Collaborative International Dictionary of English

  • brazing — kietasis litavimas statusas T sritis chemija apibrėžtis Litavimas lydmetaliais, kurių lydymosi temperatūra 450–2000 °C. atitikmenys: angl. brazing rus. пайка твердым припоем ryšiai: sinonimas – aukštatemperatūris litavimas …   Chemijos terminų aiškinamasis žodynas

  • brazing — Making an adhesion groove, fillet, or plug connection with a brazing alloy …   Dictionary of automotive terms

  • Brazing filler metal — Brazing filler metal. См. Твердый припой. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • Brazing sheet — Brazing sheet. См. Листовой припой. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • brazing metal — noun Etymology: from gerund of braze (II) : the cementing metal used in brazing compare braze, hard solder, silver solder II * * * a nonferrous metal, as copper, zinc, or nickel, or an alloy, as hard solder, used for brazing together pieces of… …   Useful english dictionary

  • brazing metal — a nonferrous metal, as copper, zinc, or nickel, or an alloy, as hard solder, used for brazing together pieces of metal. * * * …   Universalium

  • brazing flux — aukštatemperatūris fliusas statusas T sritis radioelektronika atitikmenys: angl. brazing flux vok. Hartlotflußmittel, n rus. флюс для пайки тугоплавким припоем, m pranc. flux de brasage fort, m …   Radioelektronikos terminų žodynas

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”