Technique for joining metallic parts, usually through the application of heat.Discovered in the 1st millennium AD during attempts to manipulate iron into useful shapes, the technique produced a strong, tough blade. Welding traditionally involved interlayering relatively soft and tough iron with high-carbon material, followed by hammer forging. Modern welding processes include gas welding, arc welding, and resistance welding. More recently, electron-beam welding, laser welding, and several solid-phase processes such as diffusion bonding, friction welding, and ultrasonic joining have been developed. See also brazing, soldering.
* * *Introductiontechnique used for joining metallic (metallurgy) parts usually through the application of heat. This technique was discovered during efforts to manipulate iron into useful shapes. Welded blades were developed in the first millennium AD, the most famous being those produced by Arab armourers at Damascus, Syria. The process of carburization of iron to produce hard steel was known at this time, but the resultant steel was very brittle. The welding technique—which involved interlayering relatively soft and tough iron with high-carbon material, followed by hammer forging—produced a strong, tough blade.In modern times the improvement in iron-making techniques, especially the introduction of cast iron, restricted welding to the blacksmith and the jeweler. Other joining techniques, such as fastening by bolts or rivets, were widely applied to new products, from bridges and railway engines to kitchen utensils.Modern fusion welding processes are an outgrowth of the need to obtain a continuous joint on large steel plates. Rivetting had been shown to have disadvantages, especially for an enclosed container such as a boiler. Gas welding, arc welding, and resistance welding all appeared at the end of the 19th century. The first real attempt to adopt welding processes on a wide scale was made during World War I. By 1916 the oxyacetylene process was well developed, and the welding techniques employed then are still used. The main improvements since then have been in equipment and safety. Arc welding, using a consumable electrode, was also introduced in this period, but the bare wires initially used produced brittle welds. A solution was found by wrapping the bare wire with asbestos and an entwined aluminum wire. The modern electrode, introduced in 1907, consists of a bare wire with a complex coating of minerals and metals. Arc welding was not universally used until World War II, when the urgent need for rapid means of construction for shipping, power plants, transportation, and structures spurred the necessary development work.Resistance welding, invented in 1877 by Elihu Thomson (Thomson, Elihu), was accepted long before arc welding for spot and seam joining of sheet. Butt welding for chain making and joining bars and rods was developed during the 1920s. In the 1940s the tungsten-inert gas process, using a nonconsumable tungsten electrode to perform fusion welds, was introduced. In 1948 a new gas-shielded process utilized a wire electrode that was consumed in the weld. More recently, electron-beam welding, laser welding, and several solid-phase processes such as diffusion bonding, friction welding, and ultrasonic joining have been developed.Basic principles of welding.A weld can be defined as a coalescence of metals produced by heating to a suitable temperature with or without the application of pressure, and with or without the use of a filler material.In fusion welding a heat source generates sufficient heat to create and maintain a molten pool of metal of the required size. The heat may be supplied by electricity or by a gas flame. Electric resistance welding can be considered fusion welding because some molten metal is formed.Solid-phase processes produce welds without melting the base material and without the addition of a filler metal. Pressure is always employed, and generally some heat is provided. Frictional heat is developed in ultrasonic and friction joining, and furnace heating is usually employed in diffusion bonding.The electric arc used in welding is a high-current, low-voltage discharge generally in the range 10–2,000 amperes at 10–50 volts. An arc column is complex but, broadly speaking, consists of a cathode that emits electrons, a gas plasma for current conduction, and an anode region that becomes comparatively hotter than the cathode due to electron bombardment. Therefore, the electrode, if consumable, is made positive and, if nonconsumable, is made negative. A direct current (dc) arc is usually used, but alternating current (ac) arcs can be employed.Total energy input in all welding processes exceeds that which is required to produce a joint, because not all the heat generated can be effectively utilized. Efficiencies vary from 60 to 90 percent, depending on the process; some special processes deviate widely from this figure. Heat is lost by conduction through the base metal and by radiation to the surroundings.Most metals, when heated, react with the atmosphere or other nearby metals. These reactions can be extremely detrimental to the properties of a welded joint. Most metals, for example, rapidly oxidize when molten. A layer of oxide can prevent proper bonding of the metal. Molten-metal droplets coated with oxide become entrapped in the weld and make the joint brittle. Some valuable materials added for specific properties react so quickly on exposure to the air that the metal deposited does not have the same composition as it had initially. These problems have led to the use of fluxes (flux) and inert atmospheres.In fusion welding the flux has a protective role in facilitating a controlled reaction of the metal and then preventing oxidation by forming a blanket over the molten material. Fluxes can be active and help in the process or inactive and simply protect the surfaces during joining.Inert atmospheres play a protective role similar to that of fluxes. In gas-shielded metal-arc and gas-shielded tungsten-arc welding an inert gas—usually argon—flows from an annulus surrounding the torch in a continuous stream, displacing the air from around the arc. The gas does not chemically react with the metal but simply protects it from contact with the oxygen in the air.The metallurgy of metal joining is important to the functional capabilities of the joint. The arc weld illustrates all the basic features of a joint. Three zones result from the passage of a welding arc: (1) the weld metal, or fusion zone, (2) the heat-affected zone, and (3) the unaffected zone. The weld metal is that portion of the joint that has been melted during welding. The heat-affected zone is a region adjacent to the weld metal that has not been welded but has undergone a change in microstructure or mechanical properties due to the heat of welding. The unaffected material is that which was not heated sufficiently to alter its properties.Weld-metal composition and the conditions under which it freezes (solidifies) significantly affect the ability of the joint to meet service requirements. In arc welding, the weld metal comprises filler material plus the base metal that has melted. After the arc passes, rapid cooling of the weld metal occurs. A one-pass weld has a cast structure with columnar grains extending from the edge of the molten pool to the centre of the weld. In a multipass weld, this cast structure may be modified, depending on the particular metal that is being welded.The base metal adjacent to the weld, or the heat-affected zone, is subjected to a range of temperature cycles, and its change in structure is directly related to the peak temperature at any given point, the time of exposure, and the cooling rates. The types of base metal are too numerous to discuss here, but they can be grouped in three classes: (1) materials unaffected by welding heat, (2) materials hardened by structural change, (3) materials hardened by precipitation processes.Welding produces stresses in materials. These forces are induced by contraction of the weld metal and by expansion and then contraction of the heat-affected zone. The unheated metal imposes a restraint on the above, and as contraction predominates, the weld metal cannot contract freely, and a stress is built up in the joint. This is generally known as residual stress, and for some critical applications must be removed by heat treatment of the whole fabrication. Residual stress is unavoidable in all welded structures, and if it is not controlled bowing or distortion of the weldment will take place. Control is exercised by welding technique, jigs and fixtures, fabrication procedures, and final heat treatment.There are a wide variety of welding processes. Several of the most important are discussed below.Forge welding.This original fusion technique dates from the earliest uses of iron. The process was first employed to make small pieces of iron into larger useful pieces by joining them. The parts to be joined were first shaped, then heated to welding temperature in a forge and finally hammered or pressed together. The Damascus sword, for example, consisted of wrought-iron bars hammered until thin, doubled back on themselves, and then rehammered to produce a forged weld. The larger the number of times this process was repeated, the tougher the sword that was obtained. In the Middle Ages cannons were made by welding together several iron bands, and bolts tipped with steel fired from crossbows were fabricated by forge welding. Forge welding has mainly survived as a blacksmith's craft and is still used to some extent in chain making.Shielded metal-arc welding accounts for the largest total volume of welding today. In this process an electric arc is struck between the metallic electrode and the workpiece. Tiny globules of molten metal are transferred from the metal electrode to the weld joint. Since arc welding can be done with either alternating or direct current, some welding units accommodate both for wider application. A holder or clamping device with an insulated handle is used to conduct the welding current to the electrode. A return circuit to the power source is made by means of a clamp to the workpiece.Gas-shielded arc welding, in which the arc is shielded from the air by an inert gas such as argon or helium, has become increasingly important because it can deposit more material at a higher efficiency and can be readily automated. The tungsten electrode version finds its major applications in highly alloyed sheet materials. Either direct or alternating current is used, and filler metal is added either hot or cold into the arc. Consumable electrode gas-metal arc welding with a carbon dioxide shielding gas is widely used for steel welding. Two processes known as spray arc and short-circuiting arc are utilized. Metal transfer is rapid, and the gas protection ensures a tough weld deposit.Submerged arc welding is similar to the above except that the gas shield is replaced with a granulated mineral material as a flux, which is mounded around the electrode so that no arc is visible.Plasma welding is an arc process in which a hot plasma is the source of heat. It has some similarity to gas-shielded tungsten-arc welding, the main advantages being greater energy concentration, improved arc stability, and easier operator control. Better arc stability means less sensitivity to joint alignment and arc length variation. In most plasma welding equipment, a secondary arc must first be struck to create an ionized gas stream and permit the main arc to be started. This secondary arc may utilize either a high-frequency or a direct contact start. Water cooling is used because of the high energies forced through a small orifice. The process is amenable to mechanization, and rapid production rates are possible.Thermochemical processes.One such process is gas welding. It once ranked as equal in importance to the metal-arc welding processes but is now confined to a specialized area of sheet fabrication and is probably used as much by artists as in industry. Gas welding is a fusion process with heat supplied by burning acetylene in oxygen to provide an intense, closely controlled flame. Metal is added to the joint in the form of a cold filler wire. A neutral or reducing flame is generally desirable to prevent base-metal oxidation. By deft craftsmanship very good welds can be produced, but welding speeds are very low. Fluxes aid in preventing oxide contamination of the joint.Another thermochemical process is aluminothermic (thermite) joining. It has been successfully used for both ferrous and nonferrous metals but is more frequently used for the former. A mixture of finely divided aluminum and iron oxide is ignited to produce a superheated liquid metal at about 2,800° C (5,000° F). The reaction is completed in 30 seconds to 2 minutes regardless of the size of the charge. The process is suited to joining sections with large, compact cross sections, such as rectangles and rounds. A mold is used to contain the liquid metal.Resistance welding.Spot, seam, and projection welding are resistance welding processes in which the required heat for joining is generated at the interface by the electrical resistance of the joint. Welds are made in a relatively short time (typically 0.2 seconds) using a low-voltage, high-current power source with force applied to the joint through two electrodes, one on each side. Spot welds are made at regular intervals on sheet metal that has an overlap. Joint strength depends on the number and size of the welds. Seam welding is a continuous process wherein the electric current is successively pulsed into the joint to form a series of overlapping spots or a continuous seam. This process is used to weld containers or structures where spot welding is insufficient. A projection weld is formed when one of the parts to be welded in the resistance machine has been dimpled or pressed to form a protuberance that is melted down during the weld cycle. The process allows a number of predetermined spots to be welded at one time. All of these processes are capable of very high rates of production with continuous quality control. The most modern equipment in resistance welding includes complete feedback control systems to self-correct any weld that does not meet the desired specifications.Flash welding is a resistance welding process where parts to be joined are clamped, the ends brought together slowly and then drawn apart to cause an arc or flash. Flashing or arcing is continued until the entire area of the joint is heated; the parts are then forced together and pressure maintained until the joint is formed and cooled.Low- and high-frequency resistance welding is used for the manufacture of tubing. The longitudinal joint in a tube is formed from metal squeezed into shape with edges abutted. Welding heat is governed by the current passing through the work and the speed at which the tube goes through the rolls. Welding speeds of 60 m (200 feet) per minute are possible in this process.Electron-beam welding.In electron-beam welding, the workpiece is bombarded with a dense stream of high-velocity electrons. The energy of these electrons is converted to heat upon impact. A beam-focusing device is included, and the workpiece is usually placed in an evacuated chamber to allow uninterrupted electron travel. Heating is so intense that the beam almost instantaneously vaporizes a hole through the joint. Extremely narrow deep-penetration welds can be produced using very high voltages—up to 150 kilovolts. Workpieces are positioned accurately by an automatic traverse device; for example, a weld in material 13 mm (0.5 inch) thick would only be 1 mm (0.04 inch) wide. Typical welding speeds are 125 to 250 cm (50 to 100 inches) per minute.Cold welding.Cold welding, the joining of materials without the use of heat, can be accomplished simply by pressing them together. Surfaces have to be well prepared, and pressure sufficient to produce 35 to 90 percent deformation at the joint is necessary, depending on the material. Lapped joints in sheets and cold-butt welding of wires constitute the major applications of this technique. Pressure can be applied by punch presses, rolling stands, or pneumatic tooling. Pressures of 1,400,000 to 2,800,000 kilopascals (200,000 to 400,000 pounds per square inch) are needed to produce a joint in aluminum; almost all other metals need higher pressures.Friction welding.In friction welding two workpieces are brought together under load with one part rapidly revolving. Frictional heat is developed at the interface until the material becomes plastic, at which time the rotation is stopped and the load is increased to consolidate the joint. A strong joint results with the plastic deformation, and in this sense the process may be considered a variation of pressure welding. The process is self-regulating, for, as the temperature at the joint rises, the friction coefficient is reduced and overheating cannot occur. The machines are almost like lathes in appearance. Speed, force, and time are the main variables. The process has been automated for the production of axle casings in the automotive industry.laser welding.Laser welding is accomplished when the light energy emitted from a laser source is focused upon a workpiece to fuse materials together. The limited availability of lasers of sufficient power for most welding purposes has so far restricted its use in this area. Another difficulty is that the speed and the thickness that can be welded are controlled not so much by power but by the thermal conductivity of the metals and by the avoidance of metal vaporization at the surface. Particular applications of the process with very thin materials up to 0.5 mm (0.02 inch) have, however, been very successful. The process is useful in the joining of miniaturized electrical circuitry.Diffusion bonding.This type of bonding relies on the effect of applied pressure at an elevated temperature for an appreciable period of time. Generally, the pressure applied must be less than that necessary to cause 5 percent deformation so that the process can be applied to finished machine parts. The process has been used most extensively in the aerospace industries (aerospace industry) for joining materials and shapes that otherwise could not be made—for example, multiple-finned channels and honeycomb construction. Steel can be diffusion bonded at above 1,000° C (1,800° F) in a few minutes.Ultrasonic welding.Ultrasonic joining is achieved by clamping the two pieces to be welded between an anvil and a vibrating probe or sonotrode. The vibration raises the temperature at the interface and produces the weld. The main variables are the clamping force, power input, and welding time. A weld can be made in 0.005 second on thin wires and up to 1 second with material 1.3 mm (0.05 inch) thick. Spot welds and continuous seam welds are made with good reliability. Applications include extensive use on lead bonding to integrated circuitry, transistor canning, and aluminum can bodies.Explosive welding.Explosive welding takes place when two plates are impacted together under an explosive force at high velocity. The lower plate is laid on a firm surface, such as a heavier steel plate. The upper plate is placed carefully at an angle of approximately 5° to the lower plate with a sheet of explosive material on top. The charge is detonated from the hinge of the two plates, and a weld takes place in microseconds by very rapid plastic deformation of the material at the interface. A completed weld has the appearance of waves at the joint caused by a jetting action of metal between the plates.Weldability of metals.Carbon and low-alloy steels are by far the most widely used materials in welded construction. Carbon content largely determines the weldability of plain carbon steels; at above 0.3 percent carbon some precautions have to be taken to ensure a sound joint. Low-alloy steels are generally regarded as those having a total alloying content of less than 6 percent. There are many grades of steel available, and their relative weldability varies.Aluminum and its alloys are also generally weldable. A very tenacious oxide film on aluminum tends to prevent good metal flow, however, and suitable fluxes are used for gas welding. Fusion welding is more effective with alternating current when using the gas-tungsten arc process to enable the oxide to be removed by the arc action.Copper and its alloys are weldable, but the high thermal conductivity of copper makes welding difficult. Refractory metals such as zirconium, niobium, molybdenum, tantalum, and tungsten are usually welded by the gas-tungsten arc process. Nickel is the most compatible material for joining, is weldable to itself, and is extensively used in dissimilar metal welding of steels, stainlesses, and copper alloys.
* * *